Silica (Sio₂) : 98 to 99%

Alumina (Al₂O₃) : 0.04%

Sodium Oxide (Na₂O) : 0.05%

Ferric Oxide (Fe₂O₃) : 0.04%

Magnesium Oxide (MgO) : 0.11%

Titanium Oxide (TiO₂) : 0.08%

Loss of Ignition @ 1000°C : 0.08%

Colour : Snow White

Formula : Sio₂

Fineness : 0 to 5 MM

Packing :
1.HDPE Bags
2.HDPE Bag with inner lining for moisture proofing
3.PP Bags

Our Acidic Ramming Mass is manufactured under strict supervision of qualified and experienced work force. Proper check is exercised on magnetic process to assure iron free Acidic Ramming Mass and to assure proper composition of granules according to furnace capacity. Furnace Specific Benefits: We are the only manufacturer to give material as per the furnace capacity and make of the user. The granulation of the mix are optimized keeping in view the furnace make and capacity, thus giving maximum and best results. Ramming mix is characterized by thermal stability, corrosion resistance and wear resistance because it contains less binders, fire clay and moisture compared to plastic refractories. Recommended for lining the iron melting coreless induction furnace. Premixed with binder to customers specifications. Maximum recommended use limit- 3274°F (1700°C).
SALIENT FEATURES OF OUR RAMMING MASS
•High refractoriness to with hold operating temperature
•High electrical resistivity to prevent short circuiting
•Consistent quality (purity 98.65%)
•High corrosion resistance towards steel and slag
•Grain-sizes mixed according to capacity of the furnace
•Free of iron oxide (FeO)
•Low down time for furnace lining
•Minimum expansion and contraction at high temperature (treated)
•Moisture free and sea worthily packing.

SILICA RAMMING MASS RECOMMENDED FOR :
•SS Steel
•Plain carbon steels (M.S.)
•Alloy Steels
•Low manganese and low chromium steels
•All graded cast iron
•S.G. iron and malleable iron
•Alloy cast iron